Průměr struny2,85 mm
Pracovní teplota225 - 245°C
Diameter2.85 mm ± 0.10 mm
Roundness>95%
RAL9005
Weight500 g
Colorblack
MVR 230°C/2.16 kg10 cm3/10min (ISO 1133)
MFR 230°C/2.16 kg13 gr/10 min (Test method: ISO 1133)
Elongation at break130% (Test method: ISO 527)
Tensile strength64 MPa (Test method: ISO 527)
Tensile modulus2300MPa (Test method: ISO 527)
Flexural modulus2100MPa (Test method: ISO 178)
Flexural strength94 MPa (Test method: ISO 178)
Impact strength - Charpy method 23°C9 kJ/m2 (Test method: ISO 179)
Moisture absorption0.2% (Test method: MCC Method)
Coefficient of linear thermal expansion (-20~80°C)7.3E-05 (Test method: ISO 11359-2)
Heat deflection temperature 1.80 MPa82°C (Test metod: ISO 75-1)
Transparency2% (Test method: ISO 13468)
Extrusion temperature225 - 245°C
Melting temperature235°C
Bed temperature85°C
Printing speed50 mm/s
Fan speed (can be changed to 0% is the model is warping)10%